Abstract
OBJECTIVES: The objective was to characterize the structural behaviour of indomethacin-cimetidine and naproxen-cimetidine co-amorphous systems (1 : 1 molar ratio) prepared by quench cooling, co-evaporation and ball milling.
METHODS: Powder X-ray diffraction (PXRD) and DSC were used to characterise the samples. Structural relaxation (i.e. molecular mobility) behaviour was obtained from the Kohlrausch-Williams-Watts (KWW) relationship.
KEY FINDINGS: A glass transition temperature (Tg ), on average 20 °C higher than the predicted Tg (calculated from the Fox equation), was observed in all samples. The structural relaxation was dependent on the preparative methods. At a storage temperature of 40 °C, a comparatively higher molecular mobility was observed in indomethacin-cimetidine samples prepared by ball milling (ln τ(β) = 0.8), while similar molecular mobility was found for the same sample prepared by quench cooling (ln τ(β) = 2.4) and co-evaporation (ln τ(β) = 2.5). In contrast, molecular mobility of the naproxen-cimetidine samples followed the order co-evaporation (ln τ(β) = 0.8), quench cooling (ln τ(β) = 1.6) and ball milling (ln τ(β) = 1.8).
CONCLUSION: The estimated relaxation times by the DSC-KWW method suggest that different preparative methods resulted in a variation of structural characteristics. Despite the differences in molecular mobility, all sample remained co-amorphous for up to 7 months.
Originalsprog | Engelsk |
---|---|
Tidsskrift | Journal of Pharmacy and Pharmacology |
Vol/bind | 68 |
Udgave nummer | 1 |
Sider (fra-til) | 36-45 |
Antal sider | 10 |
ISSN | 0022-3573 |
DOI | |
Status | Udgivet - jan. 2016 |